Spessore Manila

Diam. mm.

Diam. mm.

Circ. mm.

Kg/100m

Cr./bl

4

5/32

1/2

1.36

190 kgs

5

3/16

5/8

1.82

240

6

7/32

3/4

2.72

300

7

¼

7/8

3.5

370

8

5/16

1

5.4

545

9

11/32

1-1/8

6.3

620

10

3/8

1-1/4

6.8

705

12

½

1-1/2

10.5

1.065

14

9/16

1-3/4

14

1.450

16

5/8

2

19

2.03itonn

18

¾

2-1/4

22

2.44

20

13/16

2-1/2

27.5

3.25

22

7/8

2-3/4

33

3.86

24

1

3

40

4.57

26

1-1/16

3-1/4

46.8

5.35

28

1-1/8

3-1/2

53.2

6.10

30

1-1/4

3-3/4

62.7

7.00

32

1-5/16

4

70

7.90

34

1-3/8

4-1/4

80

8.80

36

1-7/16

4-1/2

89

9.65

38

1-9/16

4-3/4

100

10.80

40

1-5/8

5

110

11.941

42

1-11/16

5-1/4

123

13.10

44

1-3/4

5-1/2

134

14.23

46

1-7/8

5-3/4

147

15.50

48

1-15/16

6

158.5

16.77

50

2

6-1/4

174

18.20

52

2-1/8

6-1/2

187

19.56

54

2-3/16

6-3/4

203

20.6

56

2-1/4

7

215

22.0

58

2-5/16

7-1/4

234

23.5

60

2-3/8

7-1/2

248

25.4

64

2-1/2

8

288

29.0

72

2-7/8

9

362

35.8

80

3-1/4

10

440

43.5

88

3-1/2

11

535

51.5

96

3-3/4

12

640

60.0

 
     
  Le informazioni su esposte, sono puramente descrittive e non vincolanti. I carichi di rottura si riferiscono a tabelle R.I.N.A. per prove effettuate su corde nuove di fabbrica, prodotte con filati in alta tenacità, prima scelta. Per prodotti a tenacità normale calcolare i carichi di rottura al 50%. I pesi sono approssimativi e possono variare in ragione del 5%±.  
     