Polypropylène et Polyéthylène
| Epaisseur | Polypropylène | Polyéthylène | ||||
| Diam. mm. | Diam. inch. | Circ. inch. | Kg/100m | Cr./bl | Kg/100m | Cr./bl |
| 4 | 5/32 | 1/2 | 0.72 | 220ikgs | 0.82 | 220 kgs |
| 5 | 3/16 | 5/8 | 1.12 | 320 | 1.21 | 300 |
| 6 | 7/32 | 3/4 | 1.6 | 550 | 1.82 | 400 |
| 7 | 1/4 | 7/8 | 2.3 | 750 | 2.5 | 550 |
| 8 | 5/16 | 1 | 3.0 | 960 | 3.19 | 700 |
| 9 | 11/32 | 1-1/8 | 3.7 | 1.190 | 4.1 | 890 |
| 10 | 3/8 | 1-1/4 | 4.5 | 1.425 | 5.0 | 1.090 |
| 12 | ½ | 1-1/2 | 6.6 | 2.030 | 7.28 | 1.540 |
| 14 | 9/16 | 1-3/4 | 9.1 | 2.790 | 9.55 | 2.090 |
| 16 | 5/8 | 2 | 11.6 | 3.500 | 12.8 | 2.8itonn |
| 18 | ¾ | 2-1/4 | 14.9 | 4.450 | 16.0 | 3.5 |
| 20 | 13/16 | 2-1/2 | 17.9 | 5.370 | 20.0 | 4.3 |
| 22 | 7/8 | 2-3/4 | 22.0 | 6.500 | 24.1 | 5.1 |
| 24 | 1 | 3 | 26.0 | 7.600 | 29.6 | 6.1 |
| 26 | 1-1/16 | 3-1/4 | 30.6 | 8.800 | 34.3 | 7.0 |
| 28 | 1-1/8 | 3-1/2 | 35.5 | 10.100 | 39.1 | 8.0 |
| 30 | 1-1/4 | 3-3/4 | 40.7 | 11.400 | 45.9 | 9.0 |
| 32 | 1-5/16 | 4 | 46.0 | 12.800 | 52.3 | 10.4 |
| 34 | 1-3/8 | 4-1/4 | 52.0 | 14.400 | 59.1 | 11.6 |
| 36 | 1-7/16 | 4-1/2 | 58.0 | 16.100 | 66.0 | 13.0 |
| 38 | 1-9/16 | 4-3/4 | 64.7 | 17.700 | 72.8 | 14.3 |
| 40 | 1-5/8 | 5 | 71.5 | 19.400 | 79.7 | 15.6 |
| 42 | 1-11/16 | 5-1/4 | 80.0 | 21.400 | 87.2 | 17.2 |
| 44 | 1-3/4 | 5-1/2 | 88.5 | 23.400 | 95 | 18.8 |
| 46 | 1-7/8 | 5-3/4 | 96.0 | 25.300 | 105 | 20.6 |
| 48 | 1-15/16 | 6 | 104 | 27.200 | 115 | 22.4 |
| 50 | 2 | 6-1/4 | 113 | 29.300 | 125 | 24.3 |
| 52 | 2-1/8 | 6-1/2 | 122 | 31.500 | 135 | 26.2 |
| 54 | 2-3/16 | 6-3/4 | 132 | 33.700 | 146 | 28.2 |
| 56 | 2-1/4 | 7 | 142 | 36.000 | 158 | 30.2 |
| 58 | 2-5/16 | 7-1/4 | 152 | 38.600 | 169 | 32.2 |
| 60 | 2-3/8 | 7-1/2 | 163 | 41.200 | 180 | 34.2 |
| 64 | 2-1/2 | 8 | 185 | 46.600 | 204 | 38.6 |
| 72 | 2-7/8 | 9 | 234 | 58.500 | 260 | 48.5 |
| 80 | 3-1/4 | 10 | 290 | 72.000 | 321 | 59.8 |
| 88 | 3-1/2 | 11 | 351 | 86.400 | 388 | 72.3 |
| 96 | 3-3/4 | 12 | 417 | 102.000 | 461 | 78.8 |
Les renseignements susmentionnés sont uniquement descriptifs. La résistance se réfère au tableau R.I.N.A. pour des essais effectués sur des cordes neuves, produites avec des filés de ténacité élevée et de surchoix. Pour des produits qui ont une ténacité normale, il faut calculer la résistance au 50%. Les poids sont approximatifs et peuvent changer d’environ 5% ±.
Nylon et Polyester
| Epaisseur | Nylon | Polyester | ||||
| Diam. mm. | Diam. inch. | Circ. inch. | Kg/100m | Cr./bl | Kg/100m | Cr./bl |
| 4 | 5/32 | 1/2 | 1.05 | 320ikgs | 1.46 | 295 kgs |
| 5 | 3/16 | 5/8 | 1.64 | 500 | 2.00 | 400 |
| 6 | 7/32 | 3/4 | 2.37 | 750 | 2.91 | 565 |
| 7 | ¼ | 7/8 | 3.19 | 1.020 | 3.91 | 770 |
| 8 | 5/16 | 1 | 4.19 | 1.350 | 5.10 | 1.020 |
| 9 | 11/32 | 1-1/8 | 5.28 | 1.700 | 6.50 | 1.270 |
| 10 | 3/8 | 1-1/4 | 6.50 | 2.080 | 8.05 | 1.590 |
| 12 | ½ | 1-1/2 | 9.37 | 3.000 | 11.6 | 2.270 |
| 14 | 9/16 | 1-3/4 | 12.8 | 4.100 | 15.7 | 3.180 |
| 16 | 5/8 | 2 | 16.6 | 5.3itonn | 20.5 | 4.1itonn |
| 18 | ¾ | 2-1/4 | 21.0 | 6.7 | 26.0 | 5.1 |
| 20 | 13/16 | 2-1/2 | 26.0 | 8.3 | 31.9 | 6.3 |
| 22 | 7/8 | 2-3/4 | 31.4 | 10.0 | 38.2 | 7.6 |
| 24 | 1 | 3 | 37.3 | 12.0 | 46.0 | 9.1 |
| 26 | 1-1/16 | 3-1/4 | 43.8 | 13.8 | 54.0 | 10.6 |
| 28 | 1-1/8 | 3-1/2 | 51.0 | 15.8 | 62.8 | 12.2 |
| 30 | 1-1/4 | 3-3/4 | 58.5 | 17.8 | 72.1 | 13.8 |
| 32 | 1-5/16 | 4 | 66.4 | 20.0 | 81.9 | 15.7 |
| 34 | 1-3/8 | 4-1/4 | 74.9 | 22.0 | 92 | 17.4 |
| 36 | 1-7/16 | 4-1/2 | 83.7 | 24.8 | 104 | 19.3 |
| 38 | 1-9/16 | 4-3/4 | 93.2 | 27.4 | 116 | 21.6 |
| 40 | 1-5/8 | 5 | 104 | 30.0 | 128 | 23.9 |
| 42 | 1-11/16 | 5-1/4 | 114 | 32.9 | 141 | 26.1 |
| 44 | 1-3/4 | 5-1/2 | 126 | 35.8 | 155 | 28.4 |
| 46 | 1-7/8 | 5-3/4 | 148 | 38.9 | 169 | 30.9 |
| 48 | 1-15/16 | 6 | 150 | 42.0 | 185 | 33.5 |
| 50 | 2 | 6-1/4 | 162 | 45.4 | 200 | 36.3 |
| 52 | 2-1/8 | 6-1/2 | 175 | 48.8 | 215 | 39.1 |
| 54 | 2-3/16 | 6-3/4 | 188 | 52.4 | 231 | 41.9 |
| 56 | 2-1/4 | 7 | 203 | 56.0 | 251 | 44.7 |
| 58 | 2-5/16 | 7-1/4 | 217 | 59.9 | 269 | 47.2 |
| 60 | 2-3/8 | 7-1/2 | 233 | 63.8 | 288 | 49.8 |
| 64 | 2-1/2 | 8 | 265 | 72 | 327 | 57.9 |
| 72 | 2-7/8 | 9 | 336 | 90 | 414 | 72.1 |
| 80 | 3-1/4 | 10 | 415 | 110 | 511 | 88.4 |
| 88 | 3-1/2 | 11 | 501 | 131 | 619 | 106 |
| 96 | 3-3/4 | 12 | 597 | 154 | 736 | 125 |
Les renseignements susmentionnés sont uniquement descriptifs. La résistance se réfère au tableau R.I.N.A. pour des essais effectués sur des cordes neuves, produites avec des filés de ténacité élevée et de surchoix. Pour des produits qui ont une ténacité normale, il faut calculer la résistance au 50%. Les poids sont approximatifs et peuvent changer d’environ 5% ±.
Manile
| Epaisseur | Manile | |||
| Diam. mm. | Diam. inch. | Circ. inch. | Kg/100m | Cr./bl |
| 4 | 5/32 | 1/2 | 1.36 | 190 kgs |
| 5 | 3/16 | 5/8 | 1.82 | 240 |
| 6 | 7/32 | 3/4 | 2.72 | 300 |
| 7 | ¼ | 7/8 | 3.5 | 370 |
| 8 | 5/16 | 1 | 5.4 | 545 |
| 9 | 11/32 | 1-1/8 | 6.3 | 620 |
| 10 | 3/8 | 1-1/4 | 6.8 | 705 |
| 12 | ½ | 1-1/2 | 10.5 | 1.065 |
| 14 | 9/16 | 1-3/4 | 14 | 1.450 |
| 16 | 5/8 | 2 | 19 | 2.03itonn |
| 18 | ¾ | 2-1/4 | 22 | 2.44 |
| 20 | 13/16 | 2-1/2 | 27.5 | 3.25 |
| 22 | 7/8 | 2-3/4 | 33 | 3.86 |
| 24 | 1 | 3 | 40 | 4.57 |
| 26 | 1-1/16 | 3-1/4 | 46.8 | 5.35 |
| 28 | 1-1/8 | 3-1/2 | 53.2 | 6.10 |
| 30 | 1-1/4 | 3-3/4 | 62.7 | 7.00 |
| 32 | 1-5/16 | 4 | 70 | 7.90 |
| 34 | 1-3/8 | 4-1/4 | 80 | 8.80 |
| 36 | 1-7/16 | 4-1/2 | 89 | 9.65 |
| 38 | 1-9/16 | 4-3/4 | 100 | 10.80 |
| 40 | 1-5/8 | 5 | 110 | 11.941 |
| 42 | 1-11/16 | 5-1/4 | 123 | 13.10 |
| 44 | 1-3/4 | 5-1/2 | 134 | 14.23 |
| 46 | 1-7/8 | 5-3/4 | 147 | 15.50 |
| 48 | 1-15/16 | 6 | 158.5 | 16.77 |
| 50 | 2 | 6-1/4 | 174 | 18.20 |
| 52 | 2-1/8 | 6-1/2 | 187 | 19.56 |
| 54 | 2-3/16 | 6-3/4 | 203 | 20.6 |
| 56 | 2-1/4 | 7 | 215 | 22.0 |
| 58 | 2-5/16 | 7-1/4 | 234 | 23.5 |
| 60 | 2-3/8 | 7-1/2 | 248 | 25.4 |
| 64 | 2-1/2 | 8 | 288 | 29.0 |
| 72 | 2-7/8 | 9 | 362 | 35.8 |
| 80 | 3-1/4 | 10 | 440 | 43.5 |
| 88 | 3-1/2 | 11 | 535 | 51.5 |
| 96 | 3-3/4 | 12 | 640 | 60.0 |
Les renseignements susmentionnés sont uniquement descriptifs. La résistance se réfère au tableau R.I.N.A. pour des essais effectués sur des cordes neuves, produites avec des filés de ténacité élevée et de surchoix. Pour des produits qui ont une ténacité normale, il faut calculer la résistance au 50%. Les poids sont approximatifs et peuvent changer d’environ 5% ±.